The electrochemical insertion of alkali metals in transition metal monoxides

Electrochemical insertion of lithium was observed in monoxides ScO, TiO, and VO. The diffusion coefficient in ScO and TiO is 10-14-10-11 cm2 s-1 and in VO, it is 1-3 orders of magnitude smaller. No insertion of lithium in NbO was observed. Sodium does not enter these components at all. © 1990.

Авторы
Vondrák J.1 , Bludská J.1 , Belan V.N.2 , Lazarev V.B.2 , Bogatov Yu.E. 3
Журнал
Electrochimica Acta
Номер выпуска
1
Язык
Английский
Страницы
17-23
Статус
Опубликовано
Ссылка
Внешняя ссылка
DOI
10.1016/0013-4686(90)85030-Q
Том
35
Год
1990
Организации
  • 1 Institute of Inorganic Chemistry, Czechoslovak Academy of Science, Majakovskeho 24, 16000 Praha 6, Czech Republic
  • 2 Institute of General and Inorganic Chemistry, Academy of Science, U.S.S.R., Moscow, Russian Federation
  • 3 Patrice Lumumba University of Friendship of Nations, Russian Federation
Дата создания
19.10.2018
Дата изменения
19.10.2018
Постоянная ссылка
https://repository.rudn.ru/ru/records/article/record/1169/
Поделиться

Другие записи

NEW METHOD OF CONSTRUCTING THE 1-PYRAZOLINE RING

Статья
Prostakov N.S., Varlamov A.V., Annan H., Fomichev A.A., Aliev A.E.
Химия гетероциклических соединений. Латвийский институт органического синтеза Латвийской академии наук / Springer New York Consultants Bureau. Том 25. 1989.